PP ZPC K8009
$ 1.xxx / MT
ZPC K8009 is a kind of injection molding polypropylene resin pellets (PP material) with low temperature impact resistance, high fluidity and high toughness. Mainly used in home appliance components and general product packaging.Such as cosmetic bottle caps, cleaning product packaging, dashboards, bumpers.
Packing: 25KG/Bag
Sold by container only: 24.00 MT/Container. Quantity = number of containers.
Description
Key Benefits
High impact with good fluidity – MFI 9 g/10 min @ 230 °C / 2.16 kg; Izod notched ≈392 J/m @ 23 °C (1/8″) and ≈73 J/m @ −20 °C.
Rigid yet tough – flexural modulus ≈1078 MPa with Rockwell R 80 for shape retention.
Clean processing & dimensional stability – mould shrinkage 1.4–1.8 %; HDT 110 °C (0.45 MPa).
Regulatory ready – FDA compliant; UL 94 HB @ 1.5 mm (E162823).
Quick Specifications
| PROPERTY | TYPICAL VALUE | ISO/ASTM METHOD |
|---|---|---|
| Melt Flow Index (230 °C / 2.16 kg) | 9 g/10 min | ISO 1133 / ASTM D1238 |
| Density | 0.90 g/cm³ | ISO 1183 / ASTM D792 |
| Tensile Strength at Yield | 22 MPa | ISO 527 / ASTM D638 |
| Elongation at Break | >200 % | ISO 527 / ASTM D638 |
| Flexural Modulus | ≈1078 MPa | ISO 178 / ASTM D790 |
| Rockwell Hardness | R 80 | ISO 2039-2 / ASTM D785 |
| Izod Notched Impact, 23 °C (1/8″) | ≈392 J/m | ISO 180 / ASTM D256 |
| Izod Notched Impact, −20 °C (1/8″) | ≈73 J/m | ISO 180 / ASTM D256 |
| Heat-Deflection Temp. (0.45 MPa) | 110 °C | ISO 75 / ASTM D648 |
| Mould Shrinkage (flow) | 1.4 – 1.8 % | ISO 2577 / ASTM D955 |
| UL 94 Flammability (1.5 mm) | HB | UL 94 |
Typical Applications of TAIRIPRO® PP K8009
• Automotive parts • Battery cases • Electrical appliances • Furniture and general glossy housings.
Certifications / Standards
• UL 94 HB @ 1.5 mm (Yellow Card E162823).
• FDA compliance (food-contact).