PP FORMOSA K8009
TAIRIPRO® PP K8009 – impact copolymer polypropylene for injection-moulded parts that need high impact with good fluidity; FDA-compliant; UL 94 HB at 1.5 mm.
Sold by container only: 25.00 mt/container. Quantity = number of containers.
Key Benefits
High impact with good fluidity – MFI 9 g/10 min @ 230 °C / 2.16 kg; Izod notched ≈392 J/m @ 23 °C (1/8″) and ≈73 J/m @ −20 °C.
Rigid yet tough – flexural modulus ≈1078 MPa with Rockwell R 80 for shape retention.
Clean processing & dimensional stability – mould shrinkage 1.4–1.8 %; HDT 110 °C (0.45 MPa).
Regulatory ready – FDA compliant; UL 94 HB @ 1.5 mm (E162823).
Quick Specifications
| Property | Typical Value | ISO/ASTM Method |
|---|---|---|
| Melt Flow Index (230 °C / 2.16 kg) | 9 g/10 min | ISO 1133 / ASTM D1238 |
| Density | 0.90 g/cm³ | ISO 1183 / ASTM D792 |
| Tensile Strength at Yield | 22 MPa | ISO 527 / ASTM D638 |
| Elongation at Break | >200 % | ISO 527 / ASTM D638 |
| Flexural Modulus | ≈1078 MPa | ISO 178 / ASTM D790 |
| Rockwell Hardness | R 80 | ISO 2039-2 / ASTM D785 |
| Izod Notched Impact, 23 °C (1/8″) | ≈392 J/m | ISO 180 / ASTM D256 |
| Izod Notched Impact, −20 °C (1/8″) | ≈73 J/m | ISO 180 / ASTM D256 |
| Heat-Deflection Temp. (0.45 MPa) | 110 °C | ISO 75 / ASTM D648 |
| Mould Shrinkage (flow) | 1.4 – 1.8 % | ISO 2577 / ASTM D955 |
| UL 94 Flammability (1.5 mm) | HB | UL 94 |
Applications & Certifications
Typical Applications of TAIRIPRO® PP K8009
• Automotive parts • Battery cases • Electrical appliances • Furniture and general glossy housings.
Certifications / Standards
• UL 94 HB @ 1.5 mm (Yellow Card E162823).
• FDA compliance (food-contact).