主要特点
-
Balanced flow vs. strength – MFI 10 ml/10 min (300 °C / 1.2 kg) gives shorter cycles without sacrificing mechanical integrity.
-
High stiffness & toughness – tensile yield 65 MPa and notched Izod 75 kJ/m² keep parts rigid yet impact-durable.
-
Strong heat performance – Vicat 150 °C and HDT 128 °C @ 1.8 MPa (un-annealed) minimize warpage during painting or solder-side exposure.
-
Built-in flame protection – rated UL 94 V-2 at 2.5 mm for safer appliance and E-E uses.
3. 快速规格（典型值，23°C）
| Property | Value | ISO Method | Citation |
|---|---|---|---|
| Melt Flow Index (300 °C / 1.2 kg) | 10 ml/10 min | 1133 | |
| Density | 1.20 g/cm³ | 1183 | |
| Tensile Strength (yield) | 65 MPa | 527 | |
| Flexural Modulus | 2.4 GPa | 178 | |
| Notched Izod, 23 °C | 75 kJ/m² | 180/4A | |
| Vicat Softening (1 kg) | 150 °C | 306 | |
| HDT, 1.8 MPa (un-annealed) | 128 °C | 75/A | |
| Mould Shrinkage | 0.5 – 0.7 % | 294-4 | |
| Flammability | UL 94 V-2 (2.5 mm) | UL 94 |
4. 应用与合规性
典型应用
-
Transparent or tinted lids, guards and windows for kettles, juicers, printers.
-
E-E housings (routers, set-top boxes, power tools) needing V-2 rating.
-
Lighting components, safety shields and instrument panels.
-
Medical-labware, dispenser bodies, eyewear parts where clarity + toughness is key.
Regulatory & processing notes
-
UL Yellow Card listed under V-2 flame class; RoHS / REACH compliant (confirm current letter).
-
Dry 110 °C × 3 h; shoot 280-300 °C melt with 80-110 °C mould for glossy parts.
PC-110 提供了经典的聚碳酸酯组合特性：透明度、强度和耐热性——流动性足以满足复杂薄壁模具的加工，并具备安全规范所需的阻燃等级。